Aluminum Alloy Tube / Pipe
Aluminum alloy tubes/ pipes are easy to install and merely require minimum tooling to create complex piping systems. This metal can withstand varying temperatures and carry a wide pressure range and conditions. Whether you're looking for circular, rectangular, oval, or square hollow shapes, Yieh Corp. has got you covered.
Specification
Standard Specification
GB/T 6892
GB/T 6893
ASTM B221
EN754
EN 755
Available Size Range
-
Outside Diameter :
8 ~ 350 mm for Round
-
Outside Diameter :
15x15 ~ 250x250 mm for Square
10x20 ~ 200x250 mm for Rectangle
-
Wall Thickness :
1 ~ 40 mm
-
Length :
1,000 ~ 6,000 mm
Production Process
Extruded, Cold Drawn
Form & Image
Round, Square, Rectangle
Surface Finish
Mill Finish, unless otherwise specified
Surface Protection
Paper interleaved
Alloy and Temper
| Alloy | Temper |
|---|---|
| 5000 Series: 5052, 5083, 5754 | O, H14, H112 |
| 6000 Series: 6005, 6060, 6061, 6063, 6082, 6463 | T4, T5, T6, T66, T651, T6511 |
| Alloy Series | Chinese Standard | American Standard | European Standard |
|---|---|---|---|
| 5000 Series | 5052 | 5052 | EN AW-5052 |
| 5083 | 5083 | EN AW-5083 | |
| 5754 | - | EN AW 5754 | |
| 6000 Series | 6005 | 6005 | - |
| 6060 | 6060 | EN AW-6060 | |
| 6061 | 6061 | EN AW-6061 | |
| 6063 | 6063 | EN AW-6063 | |
| 6082 | 6082 | EN AW-6082 | |
| 6463 | 6463 | - |
| Temper | Definition |
|---|---|
| O | Annealed |
| H14 | Strain Hardened, 1/2 Hard |
| H112 | Slightly strain harden from working at an elevated temperature or from limited amount of cold work |
| T4 | Solution heat-treated and naturally aged |
| T5 | Cooled from an elevated temperature shaping process and then artificially aged |
| T6 | Solution heat-treated and then artificially aged |
| T651 | Solution heat-treated, stress-relieved by stretching a controlled amount and then artificially aged |
| T66 | Solution heat-treated and then artificially aged - mechanical property level higher than T6 achieved through special control of the process (6000 series alloys) |
| T6511 | Solution heated-treaded, stress-relieved by stretching a controlled amount and then artificially aged. Minor straightening is allowed after stretching to comply with standard tolerances |